Semicera ká10x10mm Nonpolar M-ofurufu Aluminiomu sobusitiretiti ṣe apẹrẹ daradara lati pade awọn ibeere deede ti awọn ohun elo optoelectronic to ti ni ilọsiwaju. Sobusitireti yii ṣe ẹya iṣalaye ọkọ ofurufu M-ọkọ ofurufu ti kii-polar, eyiti o ṣe pataki fun idinku awọn ipa polarization ninu awọn ẹrọ bii Awọn LED ati awọn diodes lesa, ti o yori si iṣẹ imudara ati ṣiṣe.
Awọn10x10mm Nonpolar M-ofurufu Aluminiomu sobusitiretiti ṣe iṣẹda pẹlu didara oniyebiye alailẹgbẹ, aridaju awọn iwuwo abawọn kekere ati iduroṣinṣin igbekalẹ to gaju. Eyi jẹ ki o jẹ yiyan pipe fun idagbasoke epitaxial ti awọn fiimu III-nitride ti o ni agbara giga, eyiti o ṣe pataki fun idagbasoke awọn ẹrọ optoelectronic ti iran atẹle.
Imọ-ẹrọ pipe ti Semicera ṣe idaniloju pe ọkọọkan10x10mm Nonpolar M-ofurufu Aluminiomu sobusitiretinfunni ni sisanra ti o ni ibamu ati fifẹ dada, eyiti o ṣe pataki fun fifisilẹ fiimu aṣọ ati iṣelọpọ ẹrọ. Ni afikun, iwọn iwapọ sobusitireti jẹ ki o dara fun iwadii mejeeji ati awọn agbegbe iṣelọpọ, gbigba fun lilo rọ ni ọpọlọpọ awọn ohun elo. Pẹlu igbona ti o dara julọ ati iduroṣinṣin kemikali, sobusitireti yii pese ipilẹ ti o gbẹkẹle fun idagbasoke awọn imọ-ẹrọ optoelectronic gige-eti.
| Awọn nkan | Ṣiṣejade | Iwadi | Idiwon |
| Crystal paramita | |||
| Polytype | 4H | ||
| Dada Iṣalaye aṣiṣe | <11-20>4±0.15° | ||
| Itanna paramita | |||
| Dopant | n-iru Nitrogen | ||
| Resistivity | 0.015-0.025ohm · cm | ||
| Awọn paramita ẹrọ | |||
| Iwọn opin | 150.0 ± 0.2mm | ||
| Sisanra | 350± 25 μm | ||
| Iṣalaye alapin akọkọ | [1-100]±5° | ||
| Ipari alapin akọkọ | 47,5 ± 1.5mm | ||
| Atẹle alapin | Ko si | ||
| TTV | ≤5 μm | ≤10 μm | ≤15 μm |
| LTV | ≤3 μm(5mm*5mm) | ≤5 μm(5mm*5mm) | ≤10 μm(5mm*5mm) |
| Teriba | -15μm ~ 15μm | -35μm ~ 35μm | -45μm ~ 45μm |
| Ijagun | ≤35 μm | ≤45 μm | ≤55 μm |
| Iwaju (Si-oju) líle (AFM) | Ra≤0.2nm (5μm*5μm) | ||
| Ilana | |||
| iwuwo Micropipe | <1 ea/cm2 | <10 ea/cm2 | <15 ea/cm2 |
| Irin impurities | ≤5E10atomu/cm2 | NA | |
| BPD | ≤1500 ea/cm2 | ≤3000 ea/cm2 | NA |
| TSD | ≤500 ea/cm2 | ≤1000 ea/cm2 | NA |
| Didara iwaju | |||
| Iwaju | Si | ||
| Ipari dada | Si-oju CMP | ||
| Awọn patikulu | ≤60ea/wafer (iwọn≥0.3μm) | NA | |
| Scratches | ≤5ea/mm. Akopọ ipari ≤Iwọn ila opin | Akopọ ipari≤2*Iwọn ila opin | NA |
| Peeli Orange / Pits / awọn abawọn / striations / dojuijako / idoti | Ko si | NA | |
| Awọn eerun eti / indents / fifọ / awọn awo hex | Ko si | ||
| Awọn agbegbe Polytype | Ko si | Agbegbe akojo≤20% | Agbegbe akojọpọ≤30% |
| Iwaju lesa siṣamisi | Ko si | ||
| Didara Pada | |||
| Pada pari | C-oju CMP | ||
| Scratches | ≤5ea/mm, Akopọ ipari≤2*Iwọn ila opin | NA | |
| Awọn abawọn ẹhin (awọn eerun eti/awọn indents) | Ko si | ||
| Pada roughness | Ra≤0.2nm (5μm*5μm) | ||
| Pada lesa siṣamisi | 1 mm (lati eti oke) | ||
| Eti | |||
| Eti | Chamfer | ||
| Iṣakojọpọ | |||
| Iṣakojọpọ | Epi-ṣetan pẹlu apoti igbale Olona-wafer kasẹti apoti | ||
| * Awọn akọsilẹ: "NA" tumọ si pe ko si ibeere Awọn nkan ti a ko mẹnuba le tọka si SEMI-STD. | |||